Australia AS Special Steel 209，及該型號鋼材的基本信息、化學元素成分、機械性能、力學性能、熱處理溫度、同等型號參照表等。
基本信息：
| 分類 |
種類 |
型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| Steel Grades |
|
209 |
AS |
Australia |
Australia Stainless steel |
化學成分信息(mass fraction)(wt.%) of the 209：
| 元素名稱 |
含量比例值 |
|---|
| C |
0.06 |
| Si |
1 |
| Mn |
4.00-6.00 |
| P |
0.04 |
| S |
0.030 |
| Cr |
20.5-23.5 |
| Ni |
11.5-13.5 |
| Mo |
1.50-3.00 |
機械性能信息：
| 屈服強度Rp0.2（MPa） |
抗拉強度Rm（MPa） |
沖擊率 |
伸長率 |
斷面收縮率 |
熱處理狀態(tài) |
布氏硬度（HBW） |
|---|
| 467 (≥) |
653 (≥) |
44 |
24 |
33 |
Solution and Aging, Annealing, Ausaging, Q+T,etc |
324 |
物理性質(zhì)信息：
| 溫度 |
彈性模量 |
系數(shù) |
熱導率 |
比熱容量 |
比電阻率 |
密度 |
加權(quán)系數(shù) |
|---|
| 42 |
- |
- |
|
|
0.24 |
- |
|
| 875 |
335 |
- |
21.3 |
314 |
|
- |
|
| 486 |
- |
12 |
41.2 |
|
|
442 |
321 |
熱處理信息：
| 熱處理溫度區(qū)間 |
|---|
| Heat treated : 1882°C - 1581°C |
對照表（同等等級）信息：
| 型號 |
標準 |
國家 |
應(yīng)用 |
|---|
| SS14:2092 |
SS |
Sweden |
Carbide for cutting tools |
| SS14:2092 |
SS |
Sweden |
Carbide for cutting tools |
| UNS J12092 |
GBT |
USA |
|
| UNS J82090 |
AISI |
USA |
|
| UNS J22092 |
GBT |
China |
|
| UNS J22092 |
GBT |
China |
|
| UNS J22090 |
AISI |
USA |
|
| E1209 |
UNE |
Spain |
Spain structural alloy steel |
| 209 |
AS |
Australia |
Australia Stainless steel |
| J12092 |
UNS |
USA |
Steel Castings, Alloy, Specially Heat-Treated, for PressureContaining Parts, Suitable for High-Temperature Service |
| J82090 |
UNS |
USA |
Steel Castings, Martensitic Stainless and Alloy, for Pressure-Containing Parts, Suitable for High-Temperature Service |
| J22092 |
UNS |
USA |
Steel Castings, Ferritic and Martensitic, for Pressure-Containing and Other Applications, for Low-Temperature Service |
| J22092 |
UNS |
USA |
Steel Castings, Ferritic and Martensitic, for Pressure-Containing and Other Applications, for Low-Temperature Service |
| J22090 |
UNS |
USA |
Steel Castings, Ferritic and Martensitic, for Pressure-Containing and Other Applications, for Low-Temperature Service |
| J12092 |
UNS |
USA |
Steel Castings, Alloy, Specially Heat-Treated, for PressureContaining Parts, Suitable for High-Temperature Service |
| J82090 |
UNS |
USA |
Steel Castings, Martensitic Stainless and Alloy, for Pressure-Containing Parts, Suitable for High-Temperature Service |